Analysis of X Ray Diffraction Spectra of Cholesteryl Acrylate-Indium Tin Oxide nanoparticle Composites
Afrizal, Arif Rahman, Eka Puji Astuti, Linggar Jati
Department of Chemistry Universitas Negeri Jakarta
Abstract
The blending process of cholesterol acrylate and ITO nanoparticle was performed using UV curing technique at various the concentration of ITO nanoparticles. In this research using variation concentration of ITO nanoparticles. Polymer Cho-ITO nanoparticles have succeeded in becoming a composite. Pattern of X Ray Diffraction of Cholesteryl acrylate-Indium Tin Oxide nanoparticle (Cho-ITO) at ITO 10% w/w showed peak for Cholesteryl acrylate in 2θ at 2,6782; 5,2275; dan 15,8050 with value of d spacing (001) was 32,96 Å. For ITO in 2θ at 30,6244o; 35,5105; 45,6814; 51,0400; dan 60,6473. therefore pattern of XRD of Cho-ITO at ITO 20% w/w showed peak for Cholesteryl acrylate in 2θ at 2,6372; 5,2022; dan 15,7867 dengan nilai d spacing bidang (001) sebesar 40,09 Å. For ITO in 2θ at 30,5685; 35,4428; 41,8550; 50,9846; 60,6252. increasing value of d spacing for (001), that d spacing for cholesteryl acrylate 32,60 Å when added was by ITO 10% w/w d spacing increase untuil 32,96 Å. When added ITO 20% w/w value of d spacing until 40,09 Å. This phenomenon explained that ITO nanopartikel filled space in crystalline at polymer of cholesteryl acrylate.
Keywords: XRD pattern of polymer Cholesteryl acrylate-ITO, ITO nanoparticle, Composite, Photopolymerization, UV light
Topic: Chemistry